PET Release Film
Cleansepa® is a product with a release layer coated on PET film in a high-clean environment.
Various peeling variations and anti-static (AS) type, colored type, non-silicon type, etc. are also available.
CleanSeparator® can be customized to various roll sizes according to your needs by slitting it in-house.
Non-silicone Sepa
Non-silicone light peeling sepa: 3 features
-
01.
Achieves light peeling performance that is difficult to achieve with conventional non-silicone peeling films
-
02.
Minimizes changes in peeling force after heating.
-
03.
Excellent peel force stabilization over time.
Product Lineup of PET Release Film "Non-silicone Sepa"
| Type | FILM thickness we have coated(µm) | Features(mN/50mm) | Physical Properties |
|---|---|---|---|
| HY-NS35 | 25μ, 38μ, 50μ, 75μ, 100μ | Peeling force:100 Heated peeling force:100 |
Download it here |
| HY-NS40 | 25μ, 38μ, 50μ, 75μ, 100μ | Ultra-light peeling/high heat resistance Peeling force:180 Heated peeling force:180 |
Download it here |
| HY-NS45 | 25μ, 38μ, 50μ, 75μ, 100μ | Ultra-light peeling/high heat resistance Peeling force:250 Heated peeling force:250 |
Download it here |
| HY-NS65 | 25μ, 38μ, 50μ, 75μ, 100μ | Light peeling Peeling force:500 Heated peeling force:1500 |
Download it here |
| HY-NS70 | 25μ, 38μ, 50μ, 75μ, 100μ | Light peeling Peeling force:1000 Heated peeling force:3800 |
Download it here |
| HY-NS80 | 25μ, 38μ, 50μ, 75μ, 100μ | Medium peeling Peeling force:4000 Heated peeling force:7000 |
Download it here |
| HY-NS85 | 25μ, 38μ, 50μ, 75μ, 100μ | Medium peeling Peeling force:6000 Heated peeling force:10000 |
Download it here |
| HY-NS90 | 25μ, 38μ, 50μ, 75μ, 100μ | Heavy peeling Peeling force:9000 Heated peeling force:15000 |
Download it here |
※ This table can be scrolled horizontally.
Peel force test conditions
Tape Species: Nitto 31B Tape, Peeling Rate: 300 mm/min
Peeling force: Measurement of peeling force after tape application and curing at normal room temperature for 20h
Heated peeling force: The peeling force is measured after applying the tape and curing at 70℃ for 20h.
Consult with your request regarding the depth of base materials other than the depth of the coating results described.
Clean Sepa®
Supported Size Range
| Sheet Size | A4 (210x297mm) to 1,000x1,000mm |
|---|---|
| Roll Size | 100mm to 1,200mm in width and at least 200m in length |
| Core Size | 3 or 6 inches dia. Material: paper/PE/ABS |
In-house rolling and customization as per customer requirements are possible.
Product Lineup of PET Release Film "Clean Sepa®"
| Type | Thickness/µm | Features(mN/50mm) | Physical Properties |
|---|---|---|---|
| HY-TS04GT (Colorless) |
75 | Light peeling Peeling force:40 Heated peeling force:50 |
Download it here |
| HY-TS05G (Colorless) |
75 | Light peeling Peeling force:50 Heated peeling force:60 |
Download it here |
| HY-S10 (Colorless) |
75 | Light peeling Peeling force:80 Heated peeling force:100 |
Download it here |
| HY-PS11 (Colorless) |
19 25 | Low silicone migration type /good wettability Peeling force:150 Heated peeling force:200 |
|
| HY-US20 (Colorless) |
75 | Medium peeling Peeling force:200 Heated peeling force:300 |
Download it here |
| HY-S30 (Colorless) |
75 | Heavy peeling Peeling force:350 Heated peeling force:400 |
Download it here |
| HY-S05RC-5 (Colored) |
25 38 50 | Red color Peeling force:55 Heated peeling force:60 |
Download it here |
| HY-OCS06 (Colored) |
25 38 | Orange color Peeling force:65 Heated peeling force:70 |
Download it here |
| HY-BCS30-2 (Colored) |
75 | Blue color Peeling force:350 Heated peeling force:400 |
Download it here |
※ This table can be scrolled horizontally.
Peel force test conditions
Tape Species: Nitto 31B Tape, Peeling Rate: 300 mm/min
Peeling force: Measurement of peeling force after tape application and curing at normal room temperature for 20h
Heated peeling force: The peeling force is measured after applying the tape and curing at 70℃ for 20h.