Properties Table
Search by
part number
No Results Found
Product Lineup of PET Film for Printing
| Type | Thickness/µm | Features | Physical Properties |
|---|---|---|---|
| HK-33WF | 100 125 188 250 | Both side printable film | Download it here |
| FHC-Ha | 100 125 188 | One side clear hard coat film | Download it here |
| FHC-M2a | 100 125 188 250 | One side clear hard coat film | Download it here |
| EHC-05a | 100 125 188 250 | One side anti-glare(AG) hard coat film | Download it here |
| EHC-10a | 100 125 188 250 | One side anti-glare(AG) hard coat film | Download it here |
| EHC-30a | 100 125 188 | One side anti-glare(AG) hard coat film | Download it here |
| THC-Ⅲ | 100 125 188 | One side anti-glare(AG) hard coat film | Download it here |
| BHC-Ⅲ | 100 125 188 250 | One side anti-glare(AG) hard coat film | Download it here |
| KSP-A | 125 150 188 | Both side anti-static film | Download it here |
| KSP-AN | 100 125 150 188 | Both side anti-static film | Download it here |
※ This table can be scrolled horizontally.
Product Lineup of PET Release Film "Non-silicone Sepa"
| Type | FILM thickness we have coated(µm) | Features(mN/50mm) | Physical Properties |
|---|---|---|---|
| HY-NS40 | 25μ, 38μ, 50μ, 75μ, 100μ | Ultra-light peeling/high heat resistance Peeling force:120 Heated peeling force:120 |
Download it here |
| HY-NS45 | 25μ, 38μ, 50μ, 75μ, 100μ | Ultra-light peeling/high heat resistance Peeling force:200 Heated peeling force:250 |
Download it here |
| HY-NS65 | 25μ, 38μ, 50μ, 75μ, 100μ | Light peeling Peeling force:500 Heated peeling force:1500 |
Download it here |
| HY-NS70 | 25μ, 38μ, 50μ, 75μ, 100μ | Light peeling Peeling force:1000 Heated peeling force:3800 |
Download it here |
| HY-NS80 | 25μ, 38μ, 50μ, 75μ, 100μ | Medium peeling Peeling force:4000 Heated peeling force:7000 |
Download it here |
| HY-NS85 | 25μ, 38μ, 50μ, 75μ, 100μ | Medium peeling Peeling force:6000 Heated peeling force:10000 |
Download it here |
| HY-NS90 | 25μ, 38μ, 50μ, 75μ, 100μ | Heavy peeling Peeling force:9000 Heated peeling force:15000 |
Download it here |
※ This table can be scrolled horizontally.
Peel force test conditions
Tape Species: Nitto 31B Tape, Peeling Rate: 300 mm/min
Peeling force: Measurement of peeling force after tape application and curing at normal room temperature for 20h
Heated peeling force: The peeling force is measured after applying the tape and curing at 70℃ for 20h.
Consult with your request regarding the depth of base materials other than the depth of the coating results described.
Product Lineup of PET Release Film "Clean Sepa®"
| Type | Thickness/µm | Features(mN/50mm) | Physical Properties |
|---|---|---|---|
| HY-TS04GT (Colorless) |
75 | Light peeling Peeling force:40 Heated peeling force:50 |
Download it here |
| HY-TS05G (Colorless) |
75 | Light peeling Peeling force:50 Heated peeling force:60 |
Download it here |
| HY-S10 (Colorless) |
75 | Light peeling Peeling force:80 Heated peeling force:100 |
Download it here |
| HY-PS11 (Colorless) |
19 25 | Low silicone migration type /good wettability Peeling force:150 Heated peeling force:200 |
|
| HY-US20 (Colorless) |
75 | Medium peeling Peeling force:200 Heated peeling force:300 |
Download it here |
| HY-S30 (Colorless) |
75 | Heavy peeling Peeling force:350 Heated peeling force:400 |
Download it here |
| HY-S05RC-5 (Colored) |
25 38 50 | Red color Peeling force:55 Heated peeling force:60 |
Download it here |
| HY-OCS06 (Colored) |
25 38 | Orange color Peeling force:65 Heated peeling force:70 |
Download it here |
| HY-BCS30-2 (Colored) |
75 | Blue color Peeling force:350 Heated peeling force:400 |
Download it here |
※ This table can be scrolled horizontally.
Peel force test conditions
Tape Species: Nitto 31B Tape, Peeling Rate: 300 mm/min
Peeling force: Measurement of peeling force after tape application and curing at normal room temperature for 20h
Heated peeling force: The peeling force is measured after applying the tape and curing at 70℃ for 20h.